Thickness厚度

μm

ASTM D374

23-188

Tensile Strength (MD)抗拉強度 (MD)

Mpa

ASTM D882

≥210

Tensile Strength (TD)抗拉強度 (TD)

Mpa

ASTM D882

≥230

Elongation (MD)延伸率 (MD)

%

ASTM D882

140-180

Elongation (TD)延伸率 (TD)

%

ASTM D882

120-140

Modulus (MD)彈性模量 (MD)

Mpa

ASTM D882

4500

Modulus (TD)彈性模量 (TD)

Mpa

ASTM D882

4800

Heat Shrinkage (MD)熱收縮率 (MD)

%

190℃/10min

2.0

熱收縮率 (TD)Heat Shrinkage (TD)

%

190℃/10min

0.0

Haze霧度

%

ASTM D1003

2-10

Peel Strength剝離力

g/inch

日東31B 50mm(300mm/min 180°)

4-66

Residual adhesiveness rate殘余粘著 率

%

NITTO 31B TAPE

85-97

Resistance to Solvents耐 溶劑性

Toluene甲苯

—

Good

MEK丁酮

—

Good

Ethyl Acetate乙 酸 乙 酯

—

Good

Ethanol乙醇

Excellent

Surface Wetting Tension表面張力

Dynes

19-40